Herein, charge storage behavior of graphene oxide electrode was investigated after its electrochemical activation. X-ray photoelectron spectroscopy (XPS), cyclic voltammetry (CV), galvanostatic chargedischarge method (GCD), and electrochemical impedance spectroscopy (EIS) were employed for this analysis. From XPS analysis, a decrease of atomic ratio of C=C bond was observed after electrochemical activation from 86.94 to 79.64%. Also, enhancement of specific capacitance appeared from 54.1 to 65.7 F g⁻¹ at 20 mV s⁻¹, and rectangular shape in CV became more collapsed in activated grapheme oxide electrode. In the GCD profiles, similarly, difference of resistance values at high and low cut-off potential became larger after activation, indicative of increased polarization. From EIS, detailed resistance components were compared, which reflected that the increased resistance and higher …​