By cumulative assembly of tungsten vanadate (WV₂O₇) nanorods, novel two-dimensional (2D) nanosheets of interwoven tungsten vanadate were hydrothermally formed on graphene. When as-prepared material was applied into a supercapacitor electrode using H₂SO₄ electrolyte, it was clarified that charging process was based on the pseudocapacitive reaction and the average specific capacitance was 346.4 F g⁻¹ with a high differential capacitance of 1211.4 F g^-1 at −0.1 V. Furthermore, an outstanding improvement of charge retention during cyclic voltammetry was observed (68% @ scan rate 100 mV s⁻¹) while electrode loading was as high as 5 mg cm⁻², which was practically significant since the electrode fabrication was based on conventional slurry mixing process. From Ragone plot, it was revealed that the maximum energy density was as large as 27.8 Wh kg⁻¹ at 950 W kg⁻¹, and the …​